Alumino Silicate Float Glass For Automobile Windshield Glass Processing

China float glass manufacturer for Automobile Windshield glass processing

Ultra Clear Medium Aluminosilicate Electronic Float Glass(CHIYAN-M2) is an eco-friendly ultra clear alumino-silicate glass with certain strength.

Glass Type: Float glass

Car windshields are generally made of a large curved surface as a whole, and there is a certain arc up and down. This curved glass, whether from the processing process or from the fitting point of view, is a very high technical requirements of the product, because it involves the model, strength, heat insulation, assembly and many other issues.

Standard shipping Size:1300*1100mm (5th Generation) 

Regular Thickness:

2.0mm 1.80mm 1.50mm 1.30mm

1.10mm 0.70mm 0.55mm

0.40mm 0.33mm 0.25mm

Note: The size can be customized according to customer's needs.

CHIYAN-M2’s 0.25~2.0mm thickness medium alumino-silicate glass has already been used in the market to meet a wide range of customers needs.

Application:
Float glass is widely used, divided into colored glass, float silver mirror, float glass/automobile windshield grade, float glass/all kinds of deep processing grade, float glass/scanner grade, float glass/coating grade, float glass/mirror grade. Among them, ultra-white float glass has a wide range of uses and broad market prospects, mainly used in high-grade architecture, high-grade glass processing and solar photovoltaic curtain wall fields, as well as high-grade glass furniture, decorative glass, imitation crystal products, lighting glass, precision electronics industry, special buildings, etc.

Product Composition

Ultra Clear Medium Aluminosilicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.

Chemical Tempering Process Parameter Setting Reference

Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.

Dimensions

NO.	Item	Specification	Detection Method
1	Dimensional Tolerance	1300*1100*(±2mm)	Tape Measure
2	Thickness	0.50~1.1 ±0.05m 1.3~2.0 ±0.05m	Micrometer
3	Thickness Difference	≤0.04mm	Micrometer
4	The Diagonal Difference (Perpendicularity)	≤0.3%	Tape Measure
5	Stripe	≤Level2	Point Sources of Light
6	Flatness (Before Tempering)	0.50~0.55 ≤0.15%(=h/L) 0.70~2.0 ≤0.10%(=h/L)

Appearance descriptions

NO.	Item		Specification	Detection Method
1	Effective Mass Area		All areas outside 10mm of the edge are effective mass areas.
2	Appearance Defects	Scratches	w≤0.03mm, Allowed 0.03mm＜w≤0.05mm,L≤25mm (Controlled by point defects) w＞0.05mm, Not allowed	Fluorescent Lamp 2000-2500Lux
		Bubbles	d≤0.05mm, Not counted 0.05mm＜d≤0.2mm, Numbers≤5 /m² d＞0.2mm,Not allowed
		Inclusions such as stones and sticky tin	d≤0.05mm, Not counted 0.05mm＜d≤0.2mm, Numbers≤5 /m² d＞0.2mm,Not allowed
3	Edge Defects	Chipping	Single chipping L≤2.0mm,W≤1.0mm,D≤1/2 of the thickness (as the right picture showed). The cumulative length of chipping is less than 10% of the edge length of the glass plate.
4		Cracks and missing corners	Not allowed
5	Surface stains (glass shavings, attachments, point contamination)		No stains that cannot be removed by ordinary detergents are allowed.
			d≤0.05mm, Not counted 0.05mm＜d≤0.3mm, Numbers≤5 /m² d＞0.3mm,Not allowed	The same method as appearance detection.

Packing Quantity

Packaging Diagram

Storage
Storage conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.

Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed: